| Types |
Partitioning Agent | Partitioning Agent Content (%) | Particles Smaller than 1 mm (%) | Humidity Content Máx. (%) | Acrylonitrile Content (%) | Mooney Viscosity MML 1+4 @ 100ºC | Applications |
Literature |
|
| NP 2170 |
CaCO3 | 12 | 99 | 0,7 | 30 | 57 | Low temperature flexibility and excellent wear resistance. E.g.: Sealing rings, gaskets, hoses e friction materials. |
|
| NP 1021 |
CaCO3 | 12 | 99 | 0,7 | 30 | 80 | Indicated for calendering and extrusion, excellent superficial finishing, low shrinkage, low swelling. E.g.: Hoses, conveyor belts, adhesives and sections. |
|
| NP 2007 |
CaCO3 | 12 | 99 | 0,7 | 30 | 94 | Excellent performance in dynamic applications. E.g.: Hoses, laminate floor coating, belts, friction materials and rice peeling machines. |
|
| NP 2012G |
CaCO3 | 12 | | 0,7 | 33 | 27 | For transfer and injection molding, due to its excellent flow. Presents excellent Performance in blending processes, both in open and closed blenders, quick dissolution in polar solvents. E.g.: Adhesives, retainers, rings and gaskets. |
|
| NP 3083 |
CaCO3 | 21 | 99 | 0,7 | 33 | 38 | Excellent stability, low shrinkage, elevated dimensional stability, good mechanical properties. Indicated for opaque artifacts. E.g.: PVC soles, hoses and profiles. |
|
| NP 2021 |
CaCO3 | 12 | 99 | 0,7 | 33 | 47 | General-purpose rubber for technical articles that require good oil and fuel resistance, Good processability, and a plastic modifier. E.g.: Printing blankets, flexible laminates, conveyor belts and sealing rings, sealers, gaskets, footwear, expanded artifacts, shoe soles, Synthetic leather and floors. |
|
| NP 6021 |
CaCO3 | 12 | 99 | 0,7 | 33 | 80 | Ideal para extruded artifacts in general. E.g.: Rollers, printing rollers, hoses and laminate floor coating, sections, calendared laminates, gaskets, coating fabric, and molded artifacts. |
|
| NP 6000 |
CaCO3 | 12 | 99 | 0,7 | 33 | 115 | For extruded artifacts, low swelling, elevated resistance to traction, excellent deformation by compression. E.g.: Low-hardness printing rollers, gaskets, sheets, rice peeling machines, and friction materials. |
|
| NP 2150 |
CaCO3 | 12 | 99 | 0,7 | 39 | 88 | Excellent oil and fuel resistance, good mechanical properties. E.g.: Grout, adhesives, safety soles, and friction materials. |
|
| NP 3183NV |
PVC | 12 | 99 | 0,7 | 33 | 38 | Excellent transparency and stability, low shrinkage, high dimensional stability, Excellent flow and good mechanical properties. E.g.: Electric cables, calendered laminates, PVC soles, hoses and sections. |
|
| NP 2121 |
PVC | 18 | 99 | 0,7 | 33 | 48 | General-purpose for artifacts that require good oil and grease resistance, good processability and transparency, plastic modifier. E.g.: Flexible laminates, expanded artifacts, and shoe soles. |
|
| NP 6121 |
PVC | 12 | 99 | 0,7 | 33 | 80 | Ideal for extruded products in general that require transparency. E.g.: Hoses, sections, and laminated and calendered items. |
|
| Types |
Partitioning Agent | Partitioning Agent Content (%) | Particles Smaller than 1 mm (%) | Humidity Content Máx. (%) | Styrene Content (%) | Mooney Viscosity MML 1+4 @ 100ºC | Applications |
Literature |
|
| NP 2174 |
PVC | 12 | 99 | 0,7 | 33 | 78 | Applications that require moderate chemical resistance and excellent ozone resistance. E.g.: Hoses and belts. |
|
| Types |
Partitioning Agent | Partitioning Agent Content (%) | Particles Smaller than 1 mm (%) | Humidity Content Máx. (%) | Styrene Content (%) | Mooney Viscosity MML 1+4 @ 100ºC | Applications |
Literature |
|
| SB 4022 |
CaCO3 | 12 | 99 | 0,75 | 23 | 52 | Rubber powder. Presents lower blend time, better homogenization, and lower generation of residue. Ideal for shoe soles, adhesives, seals, molded and injected artifacts.
SB |
|
Download Rubber Powder | NBR, SBR and NBR/PVC Product Line Folder